C60/1.0601

MEDIUM CARBON STEEL

NORM: PN/EN 10083-2

Anmeldung:

Steel adjusted to the parts exposed on heavy loadings and more resistant to abrasion. Such as: wheels, rims, toothed shafts, cylinders, shafts, axles, pins, eccentrics;

TECHNOLOGISCHE INFORMATIONEN::

After soft annealing, steel becomes machinable; if normalised and soft annealed, steel becomes adjusted for the mechanical cutting.

Zwischenprodukte:

After soft annealing, steel becomes machinable; if normalised and soft annealed, steel becomes adjusted for the mechanical cutting.

Mechanische Eigenschaften:

Effect of the cross-section on mechanical properties
If heat treated
Diameter d, mm Thickness of the flat bar t, mm	≤ 16 ≤ 8	16 – 40 8 – 20	40 – 100 20 – 60
Ultimate tensile strength, Rm, MPa	850 – 1000	800 – 950	750 – 900
Yield stress Re (Rp0.2), MPa	≥ 580	≥ 520	≥ 450
Elongation, A, %	≥ 11	≥ 13	≥ 14
Reduction of area, Z, %	≥ 25	≥ 30	≥ 35
If normalised
Diameter, d, mm Thickness of the flat bar t, mm	≤ 16 ≤ 16	16 – 100 16 – 100	100 – 250 100 – 250
Ultimate tensile strength, Rm, MPa	≥ 710	≥ 670	≥ 650
Yield stress Re (Rp0.2), MPa	≥ 380	≥ 340	≥ 310
Elongation, A, %	≥ 10	≥ 11	≥ 11

Technologische Verarbeitung:

Technological treatment processes			Possible application	Temperature, °C
Hot forming	Forging		+	(1050 – 850)
	Rolling		+	(1050 – 850)
Treatment	Heat treatment	Quenching	+	810-850/w,o
		Tempering	+	550 – 660
	Precipitation strengthening	Supersaturation	–	–
		Ageing	–	–
	Annealing	Normalising	+	820 – 880
		Soft annealing	+	(650 – 700)
Thermochemical treatment	Carburising		–	–
	Other		–	–

INTERNATIONALE STAHLSORTEN: